Structures by: Grin Y.
Total: 278
Er (Ga0.32 Ni0.68)5
ErGa1.6Ni3.4
Izvestiya Akademii Nauk SSSR, Metally (1983) 1983, 187-191
a=4.96Å b=4.96Å c=4.06Å
α=90° β=90° γ=120°
Dy (Ga1.5 Ni3.5)
DyGa1.5Ni3.5
Izvestiya Akademii Nauk SSSR, Metally (1983) 1983, 187-191
a=4.95Å b=4.95Å c=4.07Å
α=90° β=90° γ=120°
Ce (Fe1.85 Ga0.15)
CeFe1.85Ga0.15
Izvestiya Vysshikh Uchebnykh Zavedenii, Tsvetnaya Metallurgiya (1983) 11, 169-172
a=7.327Å b=7.327Å c=7.327Å
α=90° β=90° γ=90°
CoGaGd
CoGaGd
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1982) 1982, 57-59
a=6.982Å b=4.433Å c=7.152Å
α=90° β=90° γ=90°
CoGaPr
CoGaPr
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1982) 1982, 57-59
a=6.757Å b=4.598Å c=7.405Å
α=90° β=90° γ=90°
CoGaSm
CoGaSm
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1982) 1982, 57-59
a=6.868Å b=4.493Å c=7.253Å
α=90° β=90° γ=90°
CoErGa
CoErGa
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1982) 1982, 60-62
a=6.973Å b=4.35Å c=6.98Å
α=90° β=90° γ=90°
Co2EuGa3
Co2EuGa3
Izvestiya Akademii Nauk SSSR, Metally (1986) 1986, 204-206
a=10.126Å b=7.691Å c=5.191Å
α=90° β=90° γ=90°
Co11Ga3La6
Co11Ga3La6
Kristallografiya (1985) 30, 1077-1080
a=8.166Å b=8.166Å c=23.132Å
α=90° β=90° γ=90°
Co2GaGd6
Co2GaGd6
Ukrains'kii Fizichnii Zhurnal (Ukrainian Edition) (1984) 29, 1342-1345
a=9.4Å b=9.552Å c=9.872Å
α=90° β=90° γ=90°
(Cu0.1 Ga0.9)2 Ho
Cu0.2Ga1.8Ho
Izvestiya Akademii Nauk SSSR, Metally (1989) 1989, 214-217
a=4.322Å b=4.322Å c=3.638Å
α=90° β=90° γ=120°
(Cu0.76 Ga0.24)5 Ho
Cu3.8Ga1.2Ho
Izvestiya Akademii Nauk SSSR, Metally (1989) 1989, 214-217
a=5.065Å b=5.065Å c=4.134Å
α=90° β=90° γ=120°
(Cu5.16 Ga6.84) Ho
Cu5.16Ga6.84Ho
Izvestiya Akademii Nauk SSSR, Metally (1989) 1989, 214-217
a=8.596Å b=8.596Å c=5.166Å
α=90° β=90° γ=90°
(Cu0.32 Ga0.68)2 Ho
Cu0.64Ga1.36Ho
Izvestiya Akademii Nauk SSSR, Metally (1989) 1989, 214-217
a=4.342Å b=4.342Å c=9.096Å
α=90° β=90° γ=120°
(Cu2.2 Ga8.8) Ho3
Cu2.2Ga8.8Ho3
Izvestiya Akademii Nauk SSSR, Metally (1989) 1989, 214-217
a=4.161Å b=12.26Å c=9.719Å
α=90° β=90° γ=90°
(Cu8.84 Ga8.16) Ho2
Cu8.84Ga8.16Ho2
Izvestiya Akademii Nauk SSSR, Metally (1989) 1989, 214-217
a=8.755Å b=8.755Å c=12.758Å
α=90° β=90° γ=120°
Co5GaY5
Co5GaY5
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1984) 1984, 50-52
a=4.123Å b=10.289Å c=20.539Å
α=90° β=90° γ=90°
Eu3Ga8
Eu3Ga8
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1985) 1985, 55-58
a=4.392Å b=4.386Å c=25.866Å
α=90° β=90° γ=90°
Cs2In3
Cs2In3
Journal of the Less-Common Metals (1985) 108, 339-343
a=6.91Å b=6.91Å c=16.512Å
α=90° β=90° γ=90°
Y3 Co3 Ga
Co3GaY3
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya A: Fiziko-Matematichni Ta Tekhnichni Nauki (1978) 40, 855-858
a=4.098Å b=10.11Å c=13.01Å
α=90° β=90° γ=90°
Eu8Ga16Ge30
Eu8Ga16Ge30
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (2001) 64, 2144041-21440411
a=10.6281Å b=10.6281Å c=10.6281Å
α=90° β=90° γ=90°
Ba8Ga16Ge30
Ba8Ga16Ge30
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (2001) 64, 2144041-21440411
a=10.784Å b=10.784Å c=10.784Å
α=90° β=90° γ=90°
Ga8RuU2
Ga8RuU2
Izvestiya Akademii Nauk SSSR, Metally (1988) 1988, 202-203
a=4.2929Å b=4.2929Å c=11.059Å
α=90° β=90° γ=90°
Ca2CuGa7
Ca2CuGa7
Journal of Alloys Compd. (1994) 216, 207-211
a=4.1883Å b=4.1883Å c=11.033Å
α=90° β=90° γ=90°
Ca2Ga7Pd
Ca2Ga7Pd
Journal of Alloys Compd. (1994) 216, 207-211
a=4.2137Å b=4.2137Å c=11.0331Å
α=90° β=90° γ=90°
Ca2Ga6.76Pt1.24
Ca2Ga6.76Pt1.24
Journal of Alloys Compd. (1994) 216, 207-211
a=4.2285Å b=4.2285Å c=11.034Å
α=90° β=90° γ=90°
Ga9.36Lu3Pd1.64
Ga9.36Lu3Pd1.64
Kristallografiya (1991) 36, 898-901
a=4.2113Å b=9.467Å c=12.308Å
α=90° β=90° γ=90°
FeGa8Tm2
FeGa8Tm2
Dopovidi Akademii Nauk Ukrains'koi RSR, Seriya B: Geologichni, Khimichni ta Biologichni Nauki (1984) 1984, 45-47
a=4.212Å b=4.212Å c=11.03Å
α=90° β=90° γ=90°
(Co10 Ga7) Eu10
Co10Eu10Ga7
Kristallografiya (1991) 36, 44-48
a=10.476Å b=10.476Å c=11.045Å
α=90° β=90° γ=90°
Ga44Ni52Sm15
Ga44Ni52Sm15
Journal of Alloys Compd. (1992) 185, 19-24
a=8.771Å b=8.771Å c=25.061Å
α=90° β=90° γ=120°
(Ga0.6 Ni0.4)2 Y
Ga1.2Ni0.8Y
Neorganicheskie Materialy (1994) 30, 1409-1411
a=4.304Å b=6.99Å c=7.431Å
α=90° β=90° γ=90°
(Ga0.8 Ni0.2)2 Y
Ga1.6Ni0.4Y
Neorganicheskie Materialy (1994) 30, 1409-1411
a=4.342Å b=4.342Å c=7.249Å
α=90° β=90° γ=120°
Al2O3
Al2O3
Crystallography Reports (2008) 53, 7 1112-1118
a=3.112Å b=3.112Å c=4.988Å
α=90° β=90° γ=120°
Al3O3.52
Al3O3.52
Crystallography Reports (2008) 53, 7 1112-1118
a=7.9437Å b=7.9437Å c=7.9437Å
α=90° β=90° γ=90°
Be33Pt16Y4
Be33Pt16Y4
Dalton transactions (Cambridge, England : 2003) (2020) 49, 27 9362-9368
a=13.4849(3)Å b=13.4849(3)Å c=13.4849(3)Å
α=90° β=90° γ=90°
Yb5 Bi3
Bi3Yb5
Zeitschrift fuer Naturforschung, Teil B. Anorganische Chemie, Organische Chemie (42,1987-) (2007) 62, 935-940
a=12.6375Å b=9.7243Å c=8.4117Å
α=90° β=90° γ=90°
La7 Pd17 P12
La7P12Pd17
Zeitschrift fuer Naturforschung, Teil B. Anorganische Chemie, Organische Chemie (42,1987-) (2002) 57, 1409-1413
a=24.519Å b=4.0859Å c=13.6106Å
α=90° β=112.129° γ=90°
Ba8Ge43
Ba8Ge43
Dalton transactions (Cambridge, England : 2003) (2010) 39, 4 1078-1088
a=21.3069(3)Å b=21.3069(3)Å c=21.3069(3)Å
α=90° β=90° γ=90°
Ba8Ge43
Ba8Ge43
Dalton transactions (Cambridge, England : 2003) (2010) 39, 4 1078-1088
a=21.3079(2)Å b=21.3079(2)Å c=21.3079(2)Å
α=90° β=90° γ=90°
Ba8Ge42.1Ni3.5
Ba8Ge42.1Ni3.5
Dalton transactions (Cambridge, England : 2003) (2010) 39, 4 1071-1077
a=10.6798(2)Å b=10.6798(2)Å c=10.6798(2)Å
α=90° β=90° γ=90°
Ba8Rh2.74Si42.61
Ba8Rh2.74Si42.61
Dalton transactions (Cambridge, England : 2003) (2012) 41, 45 13960-13968
a=10.347(1)Å b=10.347(1)Å c=10.347(1)Å
α=90° β=90° γ=90°
Al6.9Ba8Si39.1
Al6.9Ba8Si39.1
Dalton transactions (Cambridge, England : 2003) (2015) 44, 28 12680-12687
a=10.4645(2)Å b=10.4645(2)Å c=10.4645(2)Å
α=90° β=90° γ=90°
B8Fe3Nb7
B8Fe3Nb7
Dalton transactions (Cambridge, England : 2003) (2016) 45, 23 9590-9600
a=8.3346(2)Å b=8.3346(2)Å c=3.2941(1)Å
α=90° β=90° γ=120°
B8Fe3Ta7
B8Fe3Ta7
Dalton transactions (Cambridge, England : 2003) (2016) 45, 23 9590-9600
a=8.2788(3)Å b=8.2788(3)Å c=3.2934(3)Å
α=90° β=90° γ=120°
B2V1
B2V1
Acta Crystallographica Section B (2015) 71, 6 777-787
a=2.9977(2)Å b=2.9977(2)Å c=3.0560(3)Å
α=90° β=90° γ=120°
B4V3
B4V3
Acta Crystallographica Section B (2015) 71, 6 777-787
a=2.9821(2)Å b=3.0601(2)Å c=13.2251(5)Å
α=90° β=90° γ=90°
Mn2Si3.5
Mn2Si3.5
Acta Crystallographica Section B (2015) 71, 6 707-712
a=5.5235(3)Å b=5.5235(3)Å c=4.3634(3)Å
α=90° β=90° γ=90°
Al5.6Fe2
Al5.6Fe2
Acta Crystallographica B (39,1983-) (1994) 50, 313-316
a=7.6559Å b=6.4154Å c=4.2184Å
α=90° β=90° γ=90°
Al11Co6Si6
Al11Co6Si6
Acta Crystallographica Section B (2007) 63, 4 551-560
a=21.3536(9)Å b=4.0420(3)Å c=7.2723(6)Å
α=90.00° β=90.00° γ=90.00°
Al11Co6Si6
Al11Co6Si6
Acta Crystallographica Section B (2007) 63, 4 551-560
a=8.0839(3)Å b=21.3536(9)Å c=8.3200(3)Å
α=90° β=119.070(10)° γ=90°
Al11Co6Si6
Al11Co6Si6
Acta Crystallographica Section B (2007) 63, 4 551-560
a=8.0839(6)Å b=14.5445(6)Å c=21.3536(9)Å
α=90° β=90° γ=90°
Al5Fe2
Al5Fe2
Acta Crystallographica Section B (1994) 50, 3 313-316
a=7.6559(8)Å b=6.4154(6)Å c=4.2184(4)Å
α=90° β=90° γ=90°
Barium niobate(1/0.92)
BaNb0.92O2.76
Zeitschrift fuer Naturforschung, Teil B. Anorganische Chemie, Organische Chemie (42,1987-) (1996) 51, 85-89
a=4.039(1)Å b=4.039(1)Å c=4.039(1)Å
α=90° β=90° γ=90°
Titanium diboride
B2Ti
Zeitschrift fuer Anorganische und Allgemeine Chemie (1996) 622, 1035-1037
a=3.0310(6)Å b=3.031Å c=3.2377(9)Å
α=90° β=90° γ=120°
Barium niobate(IV)
BaNbO3
Zeitschrift fuer Naturforschung, Teil B. Anorganische Chemie, Organische Chemie (42,1987-) (1997) 52, 153-156
a=4.039(1)Å b=4.039(1)Å c=4.039(1)Å
α=90° β=90° γ=90°
Titanium diboride
B2Ti
Zeitschrift fuer Anorganische und Allgemeine Chemie (1996) 622, 1035-1037
a=3.0292(3)Å b=3.0292(3)Å c=3.2284(3)Å
α=90° β=90° γ=120°
Cu5Se7Sn2
Cu5Se7Sn2
Chemistry of Materials (2014) 26, 18 5244
a=12.6509(3)Å b=5.6642(2)Å c=8.9319(4)Å
α=90° β=98.125(4)° γ=90°
Cu5.6Se8Sn2.4
Cu5.6Se8Sn2.4
Chemistry of Materials (2014) 26, 18 5244
a=5.74738(1)Å b=5.74738(1)Å c=11.45583(3)Å
α=90° β=90° γ=90°
BaGe5
BaGe5
Journal of the American Chemical Society (2010) 132, 10984-10985
a=10.727(1)Å b=9.2844(7)Å c=14.794(1)Å
α=90° β=90° γ=90°
K8-x Si46
K6.95Si46
Journal of the American Chemical Society (2007) 129, 5348-5349
a=10.278(1)Å b=10.278(1)Å c=10.278(1)Å
α=90° β=90° γ=90°
Na6.19Si46
Na6.19Si46
Journal of the American Chemical Society (2007) 129, 5348-5349
a=10.199(1)Å b=10.199(1)Å c=10.199(1)Å
α=90° β=90° γ=90°
Al7.62Au13.38Sr3
Al7.62Au13.38Sr3
Journal of the American Chemical Society (2014) 136, 8 3108
a=8.6644(13)Å b=8.6644(13)Å c=7.1068(14)Å
α=90.00° β=90.00° γ=120.00°
Al8.81Au12.19Sr3
Al8.81Au12.19Sr3
Journal of the American Chemical Society (2014) 136, 8 3108
a=8.6330(13)Å b=8.6330(13)Å c=7.0832(16)Å
α=90.00° β=90.00° γ=120.00°
Al1.67Au7.33Sr2
Al1.67Au7.33Sr2
Journal of the American Chemical Society (2014) 136, 8 3108
a=14.956(4)Å b=8.5641(19)Å c=8.6718(10)Å
α=90.00° β=123.860(7)° γ=90.00°
Al2.82Au6.18Sr2
Al2.82Au6.18Sr2
Journal of the American Chemical Society (2014) 136, 8 3108
a=8.4475(12)Å b=8.4475(12)Å c=21.735(4)Å
α=90.00° β=90.00° γ=120.00°
Silicon-phosphorus telluride
Si31.4P14.6Te7.4
Inorganic Chemistry (2009) 48, 3720-3730
a=9.976551(24)Å b=9.976551Å c=9.976551Å
α=90.0° β=90.0° γ=90.0°
Silicon-phosphorus telluride
Si31.4P14.6Te7.3
Inorganic Chemistry (2009) 48, 3720-3730
a=9.977718(25)Å b=9.977718Å c=9.977718Å
α=90.0° β=90.0° γ=90.0°
Mg3Ru2
Mg3Ru2
Inorganic Chemistry (2008) 47, 6051-6055
a=6.9352(6)Å b=6.9352(6)Å c=6.9352(6)Å
α=90.00° β=90.00° γ=90.00°
Al7.76Co4Si1.31
Al7.76Co4Si1.31
Inorganic Chemistry (2005) 44, 4576-4585
a=11.9935(8)Å b=4.0098(3)Å c=7.6590(8)Å
α=90° β=106.357(6)° γ=90°
?
Na2.85Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.71587(20)Å b=14.71587Å c=14.71587Å
α=90.0° β=90.0° γ=90.0°
?
Na4Si23
Inorganic Chemistry (2010) 49, 5338-5340
a=10.1959(6)Å b=10.1959Å c=10.1959Å
α=90.0° β=90.0° γ=90.0°
?
Na4Si23
Inorganic Chemistry (2010) 49, 5338-5340
a=10.1982(5)Å b=10.1982Å c=10.1982Å
α=90.0° β=90.0° γ=90.0°
?
Na4Si23
Inorganic Chemistry (2010) 49, 5338-5340
a=10.2015(7)Å b=10.2015Å c=10.2015Å
α=90.0° β=90.0° γ=90.0°
?
Na4Si23
Inorganic Chemistry (2010) 49, 5338-5340
a=10.1891(10)Å b=10.1891Å c=10.1891Å
α=90.0° β=90.0° γ=90.0°
?
Na0.4Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.64605(25)Å b=14.64605Å c=14.64605Å
α=90.0° β=90.0° γ=90.0°
Tin copper arsenide iodide
(Sn19.3Cu4.7As22),I8
Inorganic Chemistry (2005) 44, 8786-8793
a=11.1720(10)Å b=11.1720(10)Å c=11.1720(10)Å
α=90.00° β=90.00° γ=90.00°
?
Na2.72Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.70974(21)Å b=14.70974Å c=14.70974Å
α=90.0° β=90.0° γ=90.0°
?
Na2.12Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.68474(19)Å b=14.68474Å c=14.68474Å
α=90.0° β=90.0° γ=90.0°
?
Na1.73Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.66845(19)Å b=14.66845Å c=14.66845Å
α=90.0° β=90.0° γ=90.0°
?
Na1.57Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.66109(22)Å b=14.66109Å c=14.66109Å
α=90.0° β=90.0° γ=90.0°
?
Na1.37Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.65502(23)Å b=14.65502Å c=14.65502Å
α=90.0° β=90.0° γ=90.0°
?
Na1.12Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.64540(23)Å b=14.6454Å c=14.6454Å
α=90.0° β=90.0° γ=90.0°
?
Na0.85Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.64180(22)Å b=14.6418Å c=14.6418Å
α=90.0° β=90.0° γ=90.0°
?
Na0.13Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.64774(17)Å b=14.64774Å c=14.64774Å
α=90.0° β=90.0° γ=90.0°
?
NaSi17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.64285(21)Å b=14.64285Å c=14.64285Å
α=90.0° β=90.0° γ=90.0°
?
Na0.7Si17
Inorganic Chemistry (2010) 49, 5338-5340
a=14.64384(21)Å b=14.64384Å c=14.64384Å
α=90.0° β=90.0° γ=90.0°
Cu2Se3Sn
Cu2Se3Sn
Inorganic Chemistry (2013) 52, 11067-11074
a=6.9714(2)Å b=12.0787(5)Å c=13.3935(5)Å
α=90° β=99.865(5)° γ=90°
EuGaSi
EuGaSi
Inorganic chemistry (2007) 46, 21 8801-8811
a=4.1687(6)Å b=4.1687(6)Å c=4.5543(9)Å
α=90.00° β=90.00° γ=120.00°
EuGaGe
EuGaGe
Inorganic chemistry (2007) 46, 21 8801-8811
a=4.2646(6)Å b=4.2646(6)Å c=18.041(5)Å
α=90.00° β=90.00° γ=120.00°
EuGaSn
EuGaSn
Inorganic chemistry (2007) 46, 21 8801-8811
a=4.5243(5)Å b=4.5243(5)Å c=18.067(3)Å
α=90.00° β=90.00° γ=120.00°
Cerium Phosphide Silicide
Ce4P1.77Si1.23
Inorganic Chemistry (2006) 45, 18 7210-7216
a=8.9359(2)Å b=8.9359(2)Å c=8.9359(2)Å
α=90° β=90° γ=90°
AsLiSr
AsLiSr
Inorganic Chemistry (2013) 52, 8971-8978
a=7.6458(2)Å b=4.5158(1)Å c=8.0403(3)Å
α=90° β=90° γ=90°
As0.98Li0.95Sr
As0.98Li0.95Sr
Inorganic Chemistry (2013) 52, 8971-8978
a=4.49277(9)Å b=4.49277(9)Å c=8.0970(3)Å
α=90° β=90° γ=120°
P16Se1.53Si30Te6.47
P16Se1.53Si30Te6.47
Inorganic Chemistry (2012) 51, 11396-11405
a=9.929(1)Å b=9.929(1)Å c=9.929(1)Å
α=90° β=90° γ=90°